Cr4+:YAG (Y3Al5O12) crystal is ideal for passive Q-switch operation of Nd:YAG and other Nd3+ or Yb3+ doped laser crystals in the wavelength range of 900 nm to 1200 nm. Passive Q-switches or saturable absorbers provide high power laser pulses without electro-optic Q-switches, thereby reducing the package size and eliminating a high voltage power supply. A remarkable feature of Cr4+:YAG is the high damage threshold of >10 J/cm2@1064 nm, 10 ns. Its absorption band extends from 900 nm to 1200 nm and peaks around 1060 nm with a very large absorption cross-section.
Product Origin:
ChinaShipping Port:
Fuzhou, ChinaLead Time:
3-4weeks
Descriptions:
Cr4+:YAG (Y3Al5O12) Chromium Doped Yttrium AIuminum Garnet crystal is ideal for passive Q-switch operation of Nd:YAG and other Nd3+ or Yb3+ doped laser crystals in the wavelength range of 900 nm to 1200 nm.
Main applications:
1) Passively Q-switched lasers for laser rangefinders, LIDAR, and LIBS systems
2) Laser systems where short pulses are required
Advantages:
1) High chemica stability and reliability
2) Easy to operate
3) Long lifetime and good thermal conductivity
Basic properties of CrYAG
|
Chemical Formula |
Cr4+:Y3Al5O12 |
|
Crystal Structure |
Cubic |
|
Mohs Scale of Mineral Hardness |
8.5 |
|
Melting Point |
1970 °C |
|
Density, g/cm3 |
4.55 |
|
Coefficient of Thermal Conductivity @ 25°C, W x cm-1x °K-1 |
0.14 |
|
Coefficient of Thermal Expansion |
8.2 x 10-6/ ℃<100> |
|
Young's Modulus |
7.7x 106<100> |
|
Thermal Shock Resistance |
790 Wm-1 |
HGO offers CrYAG specifications:
|
Orientation: |
<100> or <110> |
|
Initial absorption coefficient |
0.1~8.5cm-1@1064nm |
|
Initial transmission |
3%~98% |
|
Wavefront Distortion: |
λ/8per inch @ 632.8 nm |
|
Dimension Tolerances： |
rods with diameter: +0.0/-0.05 mm , Length: ±0.1 mm |
|
Surface Quality: |
20/10 Scratch/Dig MIL-O-1380A |
|
Parallelism: |
< 10″ |
|
Perpendicularity: |
< 10′ |
|
Clear Aperture: |
> 90% |
|
Surface Flatness: |
< λ/10 @ 632.8 nm |
|
Chamfer: |
< 0.1 mm @ 45deg. |
|
Size |
Upon customer request |
|
Coating |
AR/HR/PR coating upon customer’s request |
|
Damage Threshold |
750MW/CM2 at 1064nm, TEM00, 10ns, 10Hz |
|
Quality Warranty Period |
One year under proper use |
Why Choose HGO ?
HG OPTRONICS.,INC. supplies very high quality of Cr4+:YAG passive Q-switch crystals Chromium Doped Yttrium AIuminum Garnet. The use of high quality starting materials for crystal growth, boule interferometry, and precise measurement of initial transmission and absorption using transmission spectroscopy and ZYGO measurements, assures that each crystal will comply with customer’s specification and perform well in laser system.
Tolerance of initial transmission can be well controlled in as high precision as 0.5% which could be very essential to some delicate laser systems.
Besides, based on HGO’s advanced bonding technology, high quality of diffusion bonding between Nd3+, Yb3+ or other ions doped YAG host laser crystals and CrYAG are available from stock or for customization.
What is more,HGO have mature solutions for different laser parameters especially in microchips solution and our engineer are very glad to discuss and provide solutions for customers.
Leave A Message
Co2+:MgAl2O4 Cospinel is a relatively new material for passive Q-switching in lasers emitting from 1.2 to 1.6 μm, in particular, for eye-safe 1.54 μm Er:glass laser, but also works at 1.44 μm and 1.34 μm wavelengths. Spinel is a hard, stable crystal that polishes well. Cobalt substitutes readily for magnesium in the Spinel host without the need for additional charge compensation ions. High absorption cross section (3.5×10-19 cm2) permits Q-switching of Er:glass laser without intracavity focusing both with flash-lamp and diode-laser pumping. Negligible excited-state absorption results in high contrast of Q-switch, i.e. the ratio of initial (small signal) to saturated absorption is higher than 10.
Read More
LiNbO3 is widely used as electro-optic modulators and Q-switches for Nd:YAG, Nd:YLF and Ti:Sapphire lasers as well as modulators for fiber optics.
Read More
Laser mirrors are fabricated with specialized coatings, which will offer high damage thresholds.
Read More
Beamsplitter Penta Prism by adding a wedge and with partial reflective coating on one of its leaning surfaces, Penta Prism can be used as Beamsplitter. Transmission/reflection (T/R) ratio of 50/50, or others for Beamsplitter Penta Prism is available upon request.
Read More
Colored glass filters are optical components that control incident wavelength by distributing an optical absorbing substance in glass.
Read More
Sapphire window retains its high strength at high temperatures, has good thermal properties and excellent transparency. It is chemically resistant to common acids and alkali at temperatures up to 1000 °C as well as to HF below 300 °C. These properties encourage its wide use in hostile environments where optical transmission in the range from the vacuum ultraviolet to the near infrared is required.
Read More
CaF2 or Calcium Fluoride is a cubic crystal with an excellent transmission from 130 nm to 10 μm and has widespread applications as transparent windows in the ultraviolet and infrared spectra.
Read More
Longpass filters are ideal for a variety of applications, such as gas monitoring, temperature, sensing, thermal imaging and motion sensing, etc. Longpass filters block shorter wavelengths and transmit longer wavelengths. Blocking can be from reflectance, absorption or a combination. Transmission in the pass band can be enhanced with an antireflection coating on the second surface.
Read More
IPv6 network supported