Cr4+:YAG (Y3Al5O12) crystal is ideal for passive Q-switch operation of Nd:YAG and other Nd3+ or Yb3+ doped laser crystals in the wavelength range of 900 nm to 1200 nm. Passive Q-switches or saturable absorbers provide high power laser pulses without electro-optic Q-switches, thereby reducing the package size and eliminating a high voltage power supply. A remarkable feature of Cr4+:YAG is the high damage threshold of >10 J/cm2@1064 nm, 10 ns. Its absorption band extends from 900 nm to 1200 nm and peaks around 1060 nm with a very large absorption cross-section.
Product Origin:
ChinaShipping Port:
Fuzhou, ChinaLead Time:
3-4weeks
Descriptions:
Cr4+:YAG (Y3Al5O12) Chromium Doped Yttrium AIuminum Garnet crystal is ideal for passive Q-switch operation of Nd:YAG and other Nd3+ or Yb3+ doped laser crystals in the wavelength range of 900 nm to 1200 nm.
Main applications:
1) Passively Q-switched lasers for laser rangefinders, LIDAR, and LIBS systems
2) Laser systems where short pulses are required
Advantages:
1) High chemica stability and reliability
2) Easy to operate
3) Long lifetime and good thermal conductivity
Basic properties of CrYAG
|
Chemical Formula |
Cr4+:Y3Al5O12 |
|
Crystal Structure |
Cubic |
|
Mohs Scale of Mineral Hardness |
8.5 |
|
Melting Point |
1970 °C |
|
Density, g/cm3 |
4.55 |
|
Coefficient of Thermal Conductivity @ 25°C, W x cm-1x °K-1 |
0.14 |
|
Coefficient of Thermal Expansion |
8.2 x 10-6/ ℃<100> |
|
Young's Modulus |
7.7x 106<100> |
|
Thermal Shock Resistance |
790 Wm-1 |
HGO offers CrYAG specifications:
|
Orientation: |
<100> or <110> |
|
Initial absorption coefficient |
0.1~8.5cm-1@1064nm |
|
Initial transmission |
3%~98% |
|
Wavefront Distortion: |
λ/8per inch @ 632.8 nm |
|
Dimension Tolerances： |
rods with diameter: +0.0/-0.05 mm , Length: ±0.1 mm |
|
Surface Quality: |
20/10 Scratch/Dig MIL-O-1380A |
|
Parallelism: |
< 10″ |
|
Perpendicularity: |
< 10′ |
|
Clear Aperture: |
> 90% |
|
Surface Flatness: |
< λ/10 @ 632.8 nm |
|
Chamfer: |
< 0.1 mm @ 45deg. |
|
Size |
Upon customer request |
|
Coating |
AR/HR/PR coating upon customer’s request |
|
Damage Threshold |
750MW/CM2 at 1064nm, TEM00, 10ns, 10Hz |
|
Quality Warranty Period |
One year under proper use |
Why Choose HGO ?
HG OPTRONICS.,INC. supplies very high quality of Cr4+:YAG passive Q-switch crystals Chromium Doped Yttrium AIuminum Garnet. The use of high quality starting materials for crystal growth, boule interferometry, and precise measurement of initial transmission and absorption using transmission spectroscopy and ZYGO measurements, assures that each crystal will comply with customer’s specification and perform well in laser system.
Tolerance of initial transmission can be well controlled in as high precision as 0.5% which could be very essential to some delicate laser systems.
Besides, based on HGO’s advanced bonding technology, high quality of diffusion bonding between Nd3+, Yb3+ or other ions doped YAG host laser crystals and CrYAG are available from stock or for customization.
What is more,HGO have mature solutions for different laser parameters especially in microchips solution and our engineer are very glad to discuss and provide solutions for customers.
Leave A Message
Co2+:MgAl2O4 Cospinel is a relatively new material for passive Q-switching in lasers emitting from 1.2 to 1.6 μm, in particular, for eye-safe 1.54 μm Er:glass laser, but also works at 1.44 μm and 1.34 μm wavelengths. Spinel is a hard, stable crystal that polishes well. Cobalt substitutes readily for magnesium in the Spinel host without the need for additional charge compensation ions. High absorption cross section (3.5×10-19 cm2) permits Q-switching of Er:glass laser without intracavity focusing both with flash-lamp and diode-laser pumping. Negligible excited-state absorption results in high contrast of Q-switch, i.e. the ratio of initial (small signal) to saturated absorption is higher than 10.
Read More
Ti:Sapphire crystal is the most widely used tunable solid-state laser material combining the supreme physical and optical properties with the extremely broad lasing range. Its lasing bandwidth can support pulses < 10fs making it the crystal of choice for femtosecond mode-locked oscillators and amplifiers. The absorption band of Ti:Sapphire centers at ~ 490 nm so it may be conveniently pumped by various laser sources such as argon ion lasers or frequency doubled Nd:YAG, Nd:YLF, Nd:YVO4 lasers at ~530nm. Laser designers are using Ti:sapphire to generate femtosecond pulses to create new industrial tools. A properly delivered femtosecond laser pulse interacts within the target leaving the surrounding area undisturbed. Newly developed femtosecond pulsed lasers micro-machine complex fine structures in glass, metal and other materials. Active waveguides can be written below the surface, integrating optical devices within the body of a substrate. Defects in photomasks can be repaired without disturbing neighbouring patterns. And it is now possible to achieve cellular resolution in vivo for medical diagnosis with femtosecond pulse lasers.
Read More
HG Optronics.,INC. can provide Metal Coated Mirror，Dielectric Coated Mirror and Dichroic Mirror which are made of substrate such as BK7, Optical glass, Fused Silica, CaF2 and so on.
Read More
Pure YAG Yttrium Aluminum Garnet is a new substrate and window material that can be used for both UV and IR optics. It is particularly useful for high-temperature and high-energy applications. The mechanical and chemical stability of YAG is comparable to sapphire crystal, but YAG is unique with no birefringence which is extremely important for some optical applications.
Read More
Co2+:MgAl2O4 Cospinel is a relatively new material for passive Q-switching in lasers emitting from 1.2 to 1.6 μm, in particular, for eye-safe 1.54 μm Er:glass laser, but also works at 1.44 μm and 1.34 μm wavelengths. Spinel is a hard, stable crystal that polishes well. Cobalt substitutes readily for magnesium in the Spinel host without the need for additional charge compensation ions. High absorption cross section (3.5×10-19 cm2) permits Q-switching of Er:glass laser without intracavity focusing both with flash-lamp and diode-laser pumping. Negligible excited-state absorption results in high contrast of Q-switch, i.e. the ratio of initial (small signal) to saturated absorption is higher than 10.
Read More
HGO grows Pr:YLF laser crystals using Czochralski technology. Pr3+:YLF has been found as promising laser material for producing visible lasers directly and UV lasers through intracavity second-harmonic generation. Very few laser materials have the necessary properties for the realization of lasing in the visible spectral range. Trivalent praseodymium (Pr3+) is known to be an interesting laser ion for use with solid-state lasers in the visible spectral range because of its energy levels scheme, providing several transitions in the red (640 nm, 3P0 to 3F2), orange (607 nm, 3P0 to 3H6), green (523 nm, 3P0 to 3H5), and dark red (720 nm, 3P0 3F3+3F4) spectral regions.
Read More
LiNbO3 is widely used as electro-optic modulators and Q-switches for Nd:YAG, Nd:YLF and Ti:Sapphire lasers as well as modulators for fiber optics.
Read More
Double Convex Lenses are used in image relay applications, or for imaging objects at close conjugates. Double Convex Lenses have positive focal lengths, along with two convex surfaces with equal radii. Aberrations will increase as the conjugate ratios increase. Double-Convex Lenses are used in a range of industries or applications. HG OPTRONICS offers Double Convex lenses with a variety of coating options.
Read More
IPv6 network supported