Cr4+:YAG crystals Chromium Doped Yttrium AIuminum Garnet

Co2+:MgAl2O4 Cospinel is a relatively new material for passive Q-switching in lasers emitting from 1.2 to 1.6 μm, in particular, for eye-safe 1.54 μm Er:glass laser, but also works at 1.44 μm and 1.34 μm wavelengths. Spinel is a hard, stable crystal that polishes well. Cobalt substitutes readily for magnesium in the Spinel host without the need for additional charge compensation ions. High absorption cross section (3.5×10-19 cm2) permits Q-switching of Er:glass laser without intracavity focusing both with flash-lamp and diode-laser pumping. Negligible excited-state absorption results in high contrast of Q-switch, i.e. the ratio of initial (small signal) to saturated absorption is higher than 10.

Our beamsplitter plates can be used in high power laser system. When using beamsplitter plates, it is important to make it in mind that the two partial beams travel in different optical paths. The optical paths depend on the incident angle and the thickness of plates.

Silicon is used as an optical window primarily in the 3 to 5 micron band and as a subsrate for production of optical filters and windows.     Silicon (Si) is grown by Czochralski pulling techniques (CZ) and contains some oxygen that causes an absorption band at 9 microns. To avoid this, material can be prepared by a Float-Zone (FZ) process. Optical silicon is generally lightly doped (5 to 40 ohm cm) for best transmission above 10 microns, and doping is usually boron (P-type) and phosphorus (N-type). After doping silicon has a further pass band: 30 to 100 microns which is effective only in very high resistivity uncompensated material.    

The Rhomboid prism application for rhomboid-prism is controlling and redirecting the optical path without affecting the image direction. They can be used to displace an optical center line for light beam folding and stereoscopic systems of different sizes.

Longpass filters are ideal for a variety of applications, such as gas monitoring, temperature, sensing, thermal imaging and motion sensing, etc. Longpass filters block shorter wavelengths and transmit longer wavelengths. Blocking can be from reflectance, absorption or a combination. Transmission in the pass band can be enhanced with an antireflection coating on the second surface.

Wedge prism is an optical element with plane-inclined surfaces, usually the faces are inclined toward one another at a very small angles.  It diverts light toward its thicker portion.  Wedge prisms can be used as isolating components. Wedges may also be used to produce a small deviation which doesnt allow return to source.

HGO grows Pr:YLF laser crystals using Czochralski technology. Pr3+:YLF has been found as promising laser material for producing visible lasers directly and UV lasers through intracavity second-harmonic generation. Very few laser materials have the necessary properties for the realization of lasing in the visible spectral range. Trivalent praseodymium (Pr3+) is known to be an interesting laser ion for use with solid-state lasers in the visible spectral range because of its energy levels scheme, providing several transitions in the red (640 nm, 3P0 to 3F2), orange (607 nm, 3P0 to 3H6), green (523 nm, 3P0 to 3H5), and dark red (720 nm, 3P0 3F3+3F4) spectral regions.

Potassium Gadolinium Tungstate (KGd(WO₄)₂) crystal is an excellent stimulated Raman laser crystal with characteristics such as a wide light transmission range, good thermal conductivity, high damage threshold, large Raman shift coefficient, and high Raman gain. It can maintain high conversion efficiency and beam quality during the Raman frequency conversion process. The KGW crystal can withstand high pump power and is suitable for pump lights of various wavelengths, making it widely used in Raman lasers, laser frequency conversion, medical imaging, photodynamic therapy, environmental monitoring, spectroscopy research, material processing, and other fields.