Cr4+:YAG (Y3Al5O12) crystal is ideal for passive Q-switch operation of Nd:YAG and other Nd3+ or Yb3+ doped laser crystals in the wavelength range of 900 nm to 1200 nm. Passive Q-switches or saturable absorbers provide high power laser pulses without electro-optic Q-switches, thereby reducing the package size and eliminating a high voltage power supply. A remarkable feature of Cr4+:YAG is the high damage threshold of >10 J/cm2@1064 nm, 10 ns. Its absorption band extends from 900 nm to 1200 nm and peaks around 1060 nm with a very large absorption cross-section.
Product Origin:
ChinaShipping Port:
Fuzhou, ChinaLead Time:
3-4weeks
Descriptions:
Cr4+:YAG (Y3Al5O12) Chromium Doped Yttrium AIuminum Garnet crystal is ideal for passive Q-switch operation of Nd:YAG and other Nd3+ or Yb3+ doped laser crystals in the wavelength range of 900 nm to 1200 nm.
Main applications:
1) Passively Q-switched lasers for laser rangefinders, LIDAR, and LIBS systems
2) Laser systems where short pulses are required
Advantages:
1) High chemica stability and reliability
2) Easy to operate
3) Long lifetime and good thermal conductivity
Basic properties of CrYAG
|
Chemical Formula |
Cr4+:Y3Al5O12 |
|
Crystal Structure |
Cubic |
|
Mohs Scale of Mineral Hardness |
8.5 |
|
Melting Point |
1970 °C |
|
Density, g/cm3 |
4.55 |
|
Coefficient of Thermal Conductivity @ 25°C, W x cm-1x °K-1 |
0.14 |
|
Coefficient of Thermal Expansion |
8.2 x 10-6/ ℃<100> |
|
Young's Modulus |
7.7x 106<100> |
|
Thermal Shock Resistance |
790 Wm-1 |
HGO offers CrYAG specifications:
|
Orientation: |
<100> or <110> |
|
Initial absorption coefficient |
0.1~8.5cm-1@1064nm |
|
Initial transmission |
3%~98% |
|
Wavefront Distortion: |
λ/8per inch @ 632.8 nm |
|
Dimension Tolerances： |
rods with diameter: +0.0/-0.05 mm , Length: ±0.1 mm |
|
Surface Quality: |
20/10 Scratch/Dig MIL-O-1380A |
|
Parallelism: |
< 10″ |
|
Perpendicularity: |
< 10′ |
|
Clear Aperture: |
> 90% |
|
Surface Flatness: |
< λ/10 @ 632.8 nm |
|
Chamfer: |
< 0.1 mm @ 45deg. |
|
Size |
Upon customer request |
|
Coating |
AR/HR/PR coating upon customer’s request |
|
Damage Threshold |
750MW/CM2 at 1064nm, TEM00, 10ns, 10Hz |
|
Quality Warranty Period |
One year under proper use |
Why Choose HGO ?
HG OPTRONICS.,INC. supplies very high quality of Cr4+:YAG passive Q-switch crystals Chromium Doped Yttrium AIuminum Garnet. The use of high quality starting materials for crystal growth, boule interferometry, and precise measurement of initial transmission and absorption using transmission spectroscopy and ZYGO measurements, assures that each crystal will comply with customer’s specification and perform well in laser system.
Tolerance of initial transmission can be well controlled in as high precision as 0.5% which could be very essential to some delicate laser systems.
Besides, based on HGO’s advanced bonding technology, high quality of diffusion bonding between Nd3+, Yb3+ or other ions doped YAG host laser crystals and CrYAG are available from stock or for customization.
What is more,HGO have mature solutions for different laser parameters especially in microchips solution and our engineer are very glad to discuss and provide solutions for customers.
Leave A Message
Co2+:MgAl2O4 Cospinel is a relatively new material for passive Q-switching in lasers emitting from 1.2 to 1.6 μm, in particular, for eye-safe 1.54 μm Er:glass laser, but also works at 1.44 μm and 1.34 μm wavelengths. Spinel is a hard, stable crystal that polishes well. Cobalt substitutes readily for magnesium in the Spinel host without the need for additional charge compensation ions. High absorption cross section (3.5×10-19 cm2) permits Q-switching of Er:glass laser without intracavity focusing both with flash-lamp and diode-laser pumping. Negligible excited-state absorption results in high contrast of Q-switch, i.e. the ratio of initial (small signal) to saturated absorption is higher than 10.
Read More
HGO grows LiF crystals in house using Czochralski technology. LiF crystal or lithium fluoride crystal is an optical material with outstanding transmittance in VUV region. It is also used for windows, prisms, and lenses in the visible and infrared in 0.104µm-7µm. LiF single crystal is sensitive to thermal shock and would be attacked by atmospheric moisture at 400°C. When working at a high temperature of 600°C, the LiF crystal softens and is slightly plastic, so it can be bent into radius plates. In addition irradiation produces color centers. Hence, users should take measures to protect LiF crystals from moisture and high energy radiation damages. What is more LiF can be cleaved along (100) plane and less commonly (110) plane. The optical characteristics are good and yet the structure is not perfect and cleavage is difficult.
Read More
The dichroic mirror is a mirror with significantly different reflection or transmission properties at two different wavelengths, it’s characterized by almost complete transmission of light at certain wavelengths and almost complete reflection of light at other wavelengths. It can be widely used in Laser technology applications.
Read More
Non-Polarizing Cube Beamsplitters also called NPBS Cube is a more sophisticated type consisting of two right- angle prisms cemented together at their hypotenuse faces.The cemented face of one prism is coated. Before cementing, with a metallic or dielectric layer having the desired reflecting properties, both in the percentage of reflection and the desired color. The absorption loss to the coating is minimal and transmission and reflection could be designed to 10%, 20%, 30%, 40%, 50%, etc.
Read More
Beamsplitter Cubes are constructed by cemented two right angle prisms. The hypotenuse of one prism is coated with polarization dielectric coating.
Read More
HGO have advanced coating machines which can meet endusers’different application requirement. We can very high laser induced damaged threshold coating with IAD, EB and IBS coating techniques , also Cr-Au, Aluminum and silver mental coating can also be available in HGO. Customers are very welcome to contact with us for further information.
Read More
Fused silica window, with low thermal expansion, providing stability and resistance to thermal shock over large temperature excursions, wide thermal operating range and high laser damage threshold, is a better choice for transmission from UV to IR.
Read More
HGO grows LBO Nonlinear crystals using flux technology. LBO crystals is an excellent nonlinear crystal.For frequency doubling(SHG),tripling(THG) of Nd:YAG,Nd:YLF,Nd:YVO4 lasers, it is one of the most useful nonlinear optical materials in ultraviolet and visible laser applications.
Read More
IPv6 network supported