Cr4+:YAG (Y3Al5O12) crystal is ideal for passive Q-switch operation of Nd:YAG and other Nd3+ or Yb3+ doped laser crystals in the wavelength range of 900 nm to 1200 nm. Passive Q-switches or saturable absorbers provide high power laser pulses without electro-optic Q-switches, thereby reducing the package size and eliminating a high voltage power supply. A remarkable feature of Cr4+:YAG is the high damage threshold of >10 J/cm2@1064 nm, 10 ns. Its absorption band extends from 900 nm to 1200 nm and peaks around 1060 nm with a very large absorption cross-section.
Product Origin:
ChinaShipping Port:
Fuzhou, ChinaLead Time:
3-4weeks
Descriptions:
Cr4+:YAG (Y3Al5O12) Chromium Doped Yttrium AIuminum Garnet crystal is ideal for passive Q-switch operation of Nd:YAG and other Nd3+ or Yb3+ doped laser crystals in the wavelength range of 900 nm to 1200 nm.
Main applications:
1) Passively Q-switched lasers for laser rangefinders, LIDAR, and LIBS systems
2) Laser systems where short pulses are required
Advantages:
1) High chemica stability and reliability
2) Easy to operate
3) Long lifetime and good thermal conductivity
Basic properties of CrYAG
|
Chemical Formula |
Cr4+:Y3Al5O12 |
|
Crystal Structure |
Cubic |
|
Mohs Scale of Mineral Hardness |
8.5 |
|
Melting Point |
1970 °C |
|
Density, g/cm3 |
4.55 |
|
Coefficient of Thermal Conductivity @ 25°C, W x cm-1x °K-1 |
0.14 |
|
Coefficient of Thermal Expansion |
8.2 x 10-6/ ℃<100> |
|
Young's Modulus |
7.7x 106<100> |
|
Thermal Shock Resistance |
790 Wm-1 |
HGO offers CrYAG specifications:
|
Orientation: |
<100> or <110> |
|
Initial absorption coefficient |
0.1~8.5cm-1@1064nm |
|
Initial transmission |
3%~98% |
|
Wavefront Distortion: |
λ/8per inch @ 632.8 nm |
|
Dimension Tolerances： |
rods with diameter: +0.0/-0.05 mm , Length: ±0.1 mm |
|
Surface Quality: |
20/10 Scratch/Dig MIL-O-1380A |
|
Parallelism: |
< 10″ |
|
Perpendicularity: |
< 10′ |
|
Clear Aperture: |
> 90% |
|
Surface Flatness: |
< λ/10 @ 632.8 nm |
|
Chamfer: |
< 0.1 mm @ 45deg. |
|
Size |
Upon customer request |
|
Coating |
AR/HR/PR coating upon customer’s request |
|
Damage Threshold |
750MW/CM2 at 1064nm, TEM00, 10ns, 10Hz |
|
Quality Warranty Period |
One year under proper use |
Why Choose HGO ?
HG OPTRONICS.,INC. supplies very high quality of Cr4+:YAG passive Q-switch crystals Chromium Doped Yttrium AIuminum Garnet. The use of high quality starting materials for crystal growth, boule interferometry, and precise measurement of initial transmission and absorption using transmission spectroscopy and ZYGO measurements, assures that each crystal will comply with customer’s specification and perform well in laser system.
Tolerance of initial transmission can be well controlled in as high precision as 0.5% which could be very essential to some delicate laser systems.
Besides, based on HGO’s advanced bonding technology, high quality of diffusion bonding between Nd3+, Yb3+ or other ions doped YAG host laser crystals and CrYAG are available from stock or for customization.
What is more,HGO have mature solutions for different laser parameters especially in microchips solution and our engineer are very glad to discuss and provide solutions for customers.
Leave A Message
Co2+:MgAl2O4 Cospinel is a relatively new material for passive Q-switching in lasers emitting from 1.2 to 1.6 μm, in particular, for eye-safe 1.54 μm Er:glass laser, but also works at 1.44 μm and 1.34 μm wavelengths. Spinel is a hard, stable crystal that polishes well. Cobalt substitutes readily for magnesium in the Spinel host without the need for additional charge compensation ions. High absorption cross section (3.5×10-19 cm2) permits Q-switching of Er:glass laser without intracavity focusing both with flash-lamp and diode-laser pumping. Negligible excited-state absorption results in high contrast of Q-switch, i.e. the ratio of initial (small signal) to saturated absorption is higher than 10.
Read More
Silicon is used as an optical window primarily in the 3 to 5 micron band and as a subsrate for production of optical filters and windows. Silicon (Si) is grown by Czochralski pulling techniques (CZ) and contains some oxygen that causes an absorption band at 9 microns. To avoid this, material can be prepared by a Float-Zone (FZ) process. Optical silicon is generally lightly doped (5 to 40 ohm cm) for best transmission above 10 microns, and doping is usually boron (P-type) and phosphorus (N-type). After doping silicon has a further pass band: 30 to 100 microns which is effective only in very high resistivity uncompensated material.
Read More
HGO grows LBO Nonlinear crystals using flux technology. LBO crystals is an excellent nonlinear crystal.For frequency doubling(SHG),tripling(THG) of Nd:YAG,Nd:YLF,Nd:YVO4 lasers, it is one of the most useful nonlinear optical materials in ultraviolet and visible laser applications.
Read More
A Plano-Convex lens causes light to focus to a point,it has a positive focal length,which is ideal for light collimation or for focusing applications utilizing monochromatic illumination, in a range of industries. HG OPTRONICS offers Plano-Convexlenses with a variety of coating options.
Read More
Color glass changed the spectral properties of optical radiation. They therefore allow scientific experiments and industrial applications where that change is necessary. You can combine color glass filters together to change the bandpass or to increase the attenuation. Color glass change the spectral properties of optical radiation. They therefore allow scientific experiments and industrial applications where that change is necessary. You can combine color glass filters together to change the band pass or to increase the attenuation.
Read More
Potassium Gadolinium Tungstate (KGd(WO₄)₂) crystal is an excellent stimulated Raman laser crystal with characteristics such as a wide light transmission range, good thermal conductivity, high damage threshold, large Raman shift coefficient, and high Raman gain. It can maintain high conversion efficiency and beam quality during the Raman frequency conversion process. The KGW crystal can withstand high pump power and is suitable for pump lights of various wavelengths, making it widely used in Raman lasers, laser frequency conversion, medical imaging, photodynamic therapy, environmental monitoring, spectroscopy research, material processing, and other fields.
Read More
YbYAG crystal is more suitable for diode-pumping than the traditional Nd-doped systems. It can be pumped at 0.94 μm laser output. Compared with the commonly used Nd:YAG crystal, Yb:YAG crystal has a much larger absorption bandwidth to reduce thermal management requirements for diode lasers, a longer upper-state lifetime, three to four times lower thermal loading per unit pump power. Yb:YAG crystal is expected to replace Nd:YAG crystal for high power diode-pumped lasers and other potential applications.
Read More
C-lens are specifically designed for fiber optics applications such as collimator, isolator, switch, collimator array and laser assembly. Compare to other gradient index lens, C-lens have several advantages including low cost, low insertion loss in long working distance, and wide working distance range. With our experienced optical design engineers, HG OPTRONICS can also provide custom designed C-lens per customer's requirement.
Read More
IPv6 network supported